- High-Magnetic-Field Annealing and Coercivity in Sintered Nd-Fe-B Magnets
抄録
Results of a systematic study concerned with the high-magnetic-field effects on the coercivity in processing various series of sintered Nd-Fe-B magnets are given. Coercivity enhancement phenomenon was observed in several series of sintered Nd-Fe-B magnets with Cu additive after annealing under magnetic fields of 10~14 T. A strong correlation was suggested between the field annealing temperature at which maximum coercivity increase was observed and the anomaly temperature in differential scanning calorimetry experiments. We found a linear relation between the room temperature coercivity Hc of the sample annealed at Ta=500℃ under magnetic field Ha for a series of samples with different Dy contents, which can be expressed as Hc=Hc(0)+ α Ha, with Hc(0) being the value for the zero-field-annealed sample and α, the coercivity enhancement factor. Although very small, α has a positive finite value in samples with 0 mass% and 2 mass% Dy. Significant increase in α value was confirmed for samples with Dy content larger than 6 mass%. This suggests the effects of higher anisotropy in paramagnetic susceptibility of Nd-rich intergranular phase containing Dy. Also introduced is the preliminary results of the grain boundary diffusion process of sinterd Nd-Fe-B samples with surface Dy layer under strong gradient magnetic fields produced by the 18 T superconducting magnets.<br>
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 76 (1), 72-80, 2012
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681458888832
-
- NII論文ID
- 130004456258
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可