• Corrosion behavior of an AZ31 magnesium alloy with deposited high purity magnesium film
• コウジュンド マグネシウム ジョウチャク マク オ ヒフク シタ AZ31 マグネシウム ゴウキン ノ フショク トクセイ

抄録

The corrosion behavior of deposited magnesium film on AZ31 alloy, pure magnesium and AZ31 alloy were studied from the measurement of electrochemical impedance spectroscopy (EIS) in 0.5 mol/dm³ sodium chloride solution (pH 6.5) at 308K. The magnesium film on AZ31 alloy was prepared by evaporation process using 3N-Mg (99.9mass%Mg) material and the thickness of the film was 100 μm. The corrosion potentials of magnesium materials became negative value with decreasing these impurities contents. Corrosion resistance of magnesium materials measured by EIS increased with decreasing these impurities. It is found that the corrosion resistance and corrosion potential of deposited magnesium film correspond to that of 6N-Mg (99.9999mass%Mg).

収録刊行物

• 軽金属

  軽金属 55 (8), 357-362, 2005

  一般社団法人 軽金属学会

キーワード

• magnesium
• deposited Mg film
• electrochemical impedance
• impurities
• corrosion resistance

詳細情報

• CRID: 1390001206340936960
• NII論文ID: 130004481777
• NII書誌ID: AN00069773
• DOI: 10.2464/jilm.55.357
• COI: 1:CAS:528:DC%2BD2MXhtVKgtLjM
• ISSN: 18808018
• ISSN: 04515994
• NDL書誌ID: 7466525
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I7466525
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
  • KAKEN
• 抄録ライセンスフラグ: 使用不可