腐食合成法によるマンガンスピネルの作製

• 世利 修美

  室蘭工業大学，

• 辻 拓也

  室蘭工業大学，

• 佐々木 大地

  室蘭工業大学大学院

書誌事項

タイトル別名

• Preparation of MnAl₂O₄ by Corrosion Synthesis
• フショク ゴウセイホウ ニ ヨル マンガンスピネル ノ サクセイ
• Preparation of MnAl2O4 by Corrosion Synthesis

抄録

Attempts have been made to obtain the manganese spinel (MnAl₂O₄) by using corrosion of manganese and aluminium chloride as catalysis. Particle diameter range of 10 − 350 micrometers was obtained when the corrosion product was hydrolyzed and calcinated at the temperature of 1573 K or more. The powder was identified as MnAl₂O₄ spinel by XRD diffraction analysis. Corrosion synthesis as one of the inorganic synthesis is explained from the viewpoint of electrochemical phenomena and considered its merits and demerits in the case of making the spinel of MnAl₂O₄.

収録刊行物

• 粉体および粉末冶金

  粉体および粉末冶金 61 (4), 153-157, 2014

  一般社団法人 粉体粉末冶金協会

キーワード

• MnAl₂O₄ spinel
• aluminum
• double oxide
• corrosion synthesis

詳細情報

• CRID: 1390001206311187712
• NII論文ID: 130004678651
• NII書誌ID: AN00222724
• DOI: 10.2497/jjspm.61.153
• COI: 1:CAS:528:DC%2BC2cXhtFWms7%2FE
• ISSN: 18809014
• ISSN: 05328799
• NDL書誌ID: 025485945
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I025485945
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可