Influence of the Initial Texture on Texture Formation of High Temperature Deformation in AZ80 Magnesium Alloy
-
- Kim Kwon-Hoo
- Department of Metallurgical Engineering, Pukyong National University
-
- Okayasu Kazuto
- Faculty of Engineering, Graduate School of Yokohama National University
-
- Fukutomi Hiroshi
- Faculty of Engineering, Graduate School of Yokohama National University
この論文をさがす
抄録
The texture formation mechanism during high temperature deformation is investigated on AZ80 magnesium alloy. Three kinds of specimens with different initial textures were machined out from rolled plate having a ⟨0001⟩ texture. Plane strain compression tests were conducted at 723 K, 5.0 × 10−2 s−1 and strains ranging from −0.4 to −1.0. Development of (0001)<10\bar{1}0> component is confirmed regardless of the initial texture. It is concluded that the development of (0001)<10\bar{1}0> component can be attributed to the grain boundary migration during deformation. Besides (0001)<10\bar{1}0> component, several texture components appeared depending on the initial texture.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 56 (1), 17-22, 2015
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679229392512
-
- NII論文ID
- 40020318815
- 130004704651
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 026013876
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可