ポリピロールを用いた電気化学バイオセンサの機能デザイン

DOI Web Site Web Site 参考文献10件

書誌事項

タイトル別名
  • Functional Design of Electrochemical Biosensors Using Polypyrrole
  • ポリピロール オ モチイタ デンキ カガク バイオセンサ ノ キノウ デザイン

この論文をさがす

抄録

In order to improve biosensor performance namely, the sensitivity, response time, and linear range values, novel amerometric polypyrrole (PPy) glucose biosensors, achieved by three different immobilizing techniques namely, physical adsorption, coentrapment and a two steps method of coentrapment superimposed with physical adsorption had been studied. Different enzyme loading and material properties resulted in varied immobilizing techniques lead to dissimilarities in characteristics. In this study, Pt coated AnodiscTMs with 0.2 µm maximum pore size were used as electrodes to polymerize PPy at 0.3 mAcm-2 using a solution containing 0.05 mol/l pyrrole and 0.1 M NaPF6. The polymerization time was optimized to 90 s. In the coentrapment method, glucose oxidase (GOx) (1 mg/ml) was added to the monomer solution while an aliquot of GOx (5 µl) was placed on the pre-polymerized electrode for physical adsorption. A combined procedure of these two techniques was used as the last immobilization technique. Physical adsorption method gave a sensitivity of 3 mAcm-2 (mol/l)-1 and a linear range of 0.5-13×10-3 mol/l with a response time of a 3 s. Sensitivity in the case of coentrapment was 3.75 mAcm-2 (mol/l)-1 while it showed a value of 4.45 mAcm-2 (mol/l)-1 in two step immobilization thus giving 25 and 48 % increases respectively. Response times of 9 and 8 s in latter cases reveal the possible repercussion taking place at enzyme immobilization in three dimensional (3-D) PPy matrix and the delay occur in glucose to reach the enzyme. Linear range of the two step method was extended up to 16×10-3 mol/l due to the reinforced enzyme loading.

収録刊行物

参考文献 (10)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ