- Effects of Drawing Conditions after Ni-Plating on Corrosion Resistance of Ni-Plated Steel Wire
- Niメッキ アト ノ シンセン カコウ ジョウケン ガ タイショクセイ ニ オヨボス エイキョウ
この論文をさがす
抄録
Ni-plated steel wires used for springs in electrical appliances and other devices have good corrosion resistance. They are expected as alternatives to stainless-steel wire in a mildly corrosive environment. Further corrosion resistance is required for applications in automobile parts. The reasons for the low corrosion resistance are assumed to be a decrease in the average Ni-plated thickness upon drawing, and the variation in the Ni-plating thickness owing to the irregular deformation of the interface between the Ni-plating and the base material. In this study, the effects of the drawing conditions and Ni-plated thickness on corrosion resistance were examined. Under drawing conditions, the reduction in area varies from 0% to 40%. On the other hand, Ni-plated thickness is in the range from 2μm to 30μm. It is found that the drawing with a 10% reduction in area after applying Ni-plating thicker than 30μm are the most effective conditions for corrosion resistance.
収録刊行物
-
- 塑性と加工
-
塑性と加工 56 (651), 317-321, 2015
一般社団法人 日本塑性加工学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681475049088
-
- NII論文ID
- 130005067119
-
- NII書誌ID
- AN00135062
-
- ISSN
- 18820166
- 00381586
-
- NDL書誌ID
- 026389169
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可