- Effects of Aliquat 336 Concentration and Solvent Composition on Amount of Aliquat 336 Impregnated and Liquid Permeability of Aliquat 336-Impregnated Porous Hollow-Fiber Membrane
- Aliquat 336タントクタコウセイ チュウクウシ マク ノ タンジリョウ ト エキ トウカセイ ニ オヨボス Aliquat 336 ノウド ト ヨウバイ ソセイ ノ コウカ
この論文をさがす
抄録
A basic extractant Aliquat 336 dissolved in a mixture of water and ethanol was impregnated to carboxypentyl-amino (CPA)-group-containing polymer chains grafted onto a porous hollow-fiber membrane. The CPA group was introduced into the graft chain by a reaction of the epoxy group of poly-glycidyl methacrylate (GMA) chain grafted onto the porous hollow-fiber membrane with 6-aminohexanoic acid. The electrostatic interaction between the carboxyl moiety of the CPA group and the quarternary ammonium group of Aliquat 336 gave rise to a high-density impregnation of Aliquat 336. A higher water volume fraction in the mixture of water and ethanol used as a solvent of Aliquat 336 induced a higher extension of the graft chain, resulting in an increase in the amount of Aliquat 336 impregnated. In addition, a higher Aliquat 336 concentration produced a higher amount of Aliquat 336 impregnated. A water volume fraction of 0.33 and an Aliquat 336 concentration of 10% were selected on the basis of a trade-off between the amount of Aliquat 336 impregnated and the liquid permeability. The pure water flux of porous hollow-fiber membrane with 1.2 mol Aliquat 336 per kg GMA-grafted porous hollow-fiber membrane was 2.5 m/h at 0.1 MPa and 298 K. During the permeation of 100 mg-Pt/L platinum chloride solution (pH 4.0) through the pores of the Aliquat 336- impregnated porous hollow-fiber membrane, platinum complex ions (PtCl6 2–) were captured by Aliquat 336 impregnated to the graft chain, while the permeation pressure required for a constant flow rate increased. The breakthrough binding capacity of the Aliquat 336-impregnated porous hollow-fiber membrane for platinum was 0.37 mol per kg of the GMA-grafted porous hollow-fiber membrane.
収録刊行物
-
- 膜
-
膜 32 (3), 168-174, 2007
日本膜学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681398388992
-
- NII論文ID
- 130005077801
-
- NII書誌ID
- AN0023215X
-
- ISSN
- 18846440
- 03851036
- http://id.crossref.org/issn/03851036
-
- NDL書誌ID
- 8836176
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可