Synthesis and electrochemical properties of Li<sub>4</sub>Ti<sub>5</sub>O<sub>12</sub>/C nano-powders by pulse jet spray pyrolysis
-
- FURUKAWA Yasuhiko
- Graduate School of Engineering, Advanced Interdisciplinary Science and Technology, University of Fukui
-
- OGIHARA Takashi
- Graduate School of Engineering, Advanced Interdisciplinary Science and Technology, University of Fukui
-
- KODERA Takayuki
- Graduate School of Material Science and Engineering, University of Fukui
抄録
Li4Ti5O12/C nano-powders were successfully synthesized at 500°C through the pulse jet spray pyrolysis with use of a citric acid aqueous solution. As-prepared Li4Ti5O12/C nano-particles had spherical and irregular shapes with an average size of 50 nm. As-prepared Li4Ti5O12/C nano-particles had a spinel phase with high crystallinity and a homogeneous chemical composition. The carbon content was 10 wt % in the Li4Ti5O12 nano-powders. A 2032 type coin cell was used to examine electrochemical properties of the Li4Ti5O12/C anode. The discharge capacity of Li4Ti5O12/C anode exhibited 170 at 1 C and 120 mAh·g−1 at 20 C, respectively. The discharge capacity of the Li4Ti5O12/C anode maintained 96% of the initial discharge capacity after 500th cycle at 10 C and room temperature. The discharge capacity of the Li4Ti5O12/C anode exhibited 160 mAh·g−1 at 10 C and 50°C and maintained 98% of the initial discharge capacity after 100th cycle.
収録刊行物
-
- Journal of the Ceramic Society of Japan
-
Journal of the Ceramic Society of Japan 124 (5), 613-616, 2016
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205287795968
-
- NII論文ID
- 130005149947
-
- ISSN
- 13486535
- 18820743
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可