Temperature dependence of unipolar fatigue behavior of lead-free alkali niobate ceramics
-
- MARTIN Alexander
- Frontier Research Institute for Materials Science, Nagoya Institute of Technology
-
- KAKIMOTO Ken-ichi
- Frontier Research Institute for Materials Science, Nagoya Institute of Technology
-
- HATANO Keiichi
- Materials R&D Department, R&D Laboratory, TAIYO YUDEN CO., LTD.
-
- DOSHIDA Yutaka
- Materials R&D Department, R&D Laboratory, TAIYO YUDEN CO., LTD.
抄録
The unipolar fatigue behavior of undoped Li0.06Na0.52K0.42NbO3 (LNKN6-a) and the same compound with additives (LNKN6-b) were observed. Unipolar cycling was performed between room temperature and 150°C under a high unipolar electric field of 4 kV/mm. LNKN6-a fatigued under crack formation throughout the examined temperature range. The switchable polarization 2Pr of LNKN6-a decreased for 20% (=2 µC/cm2) at 150°C. In contrast, mechanical degradation was not observed in LNKN6-b. The switchable polarization 2Pr of LNKN6-b decreased for 15% (=3.2 µC/cm2) at 150°C. It should be noted that at 50°C, fatigue-free behavior was observed for LNKN6-b over at least 106 cycles. The influence of phase transition on this fatigue-free behavior was discussed.
収録刊行物
-
- Journal of the Ceramic Society of Japan
-
Journal of the Ceramic Society of Japan 124 (6), 730-736, 2016
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680262089344
-
- NII論文ID
- 130005155652
-
- ISSN
- 13486535
- 18820743
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可