XRDおよびEBSDを用いた23Cr-45Ni-7W合金溶接部のひずみ評価

DOI Web Site Web Site 被引用文献1件 参考文献18件

書誌事項

タイトル別名
  • Strain Analysis of Weld Joint of 23Cr-45Ni-7W Alloy by XRD and EBSD Method
  • XRD オヨビ EBSD オ モチイタ 23Cr-45Ni-7W ゴウキン ヨウセツブ ノ ヒズミ ヒョウカ

この論文をさがす

抄録

<p>The residual strain of 23Cr-45Ni-7W Alloy welds was estimated by the change in the dislocation density and the average misorientation within grains. X-ray diffraction was used to measure the dislocation density by the modified Williamson-Hall method and the modified Warren-Averbach method. EBSD technique was used to measure the orientation in order to calculate the grain orientation spread (GOS) as the average misorientation within grains. Tensile tests were conducted at room temperature and were interrupted to prepare a number of specimens with different residual strain. The changes in the dislocation density and GOS with the strain were investigated using the interrupted specimens and the heat-affected zone in 23Cr-45Ni-7W Alloy welds. The dislocation density and GOS increased approximately linearly with increase in the residual strain. The residual strain of the heat-affected zone in 23Cr-45Ni-7W Alloy welds was evaluated from the linear relationships. The residual strain near the bond line estimated by the dislocation density was 3.7%;the estimated residual strain decreased with increases in the distance from the bond line. At 10 mm away from the bond line, the residual strain became less than 1%. The change in the residual strain near the bond line estimated by GOS showed a similar tendency.</p>

収録刊行物

  • 材料

    材料 66 (1), 51-57, 2017

    公益社団法人 日本材料学会

被引用文献 (1)*注記

もっと見る

参考文献 (18)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ