Formation and photoluminescence of zirconia dendrites in borosilicate glass-ceramics
-
- NOBUTA Yasuhiro
- Department of Applied Physics, Tohoku University
-
- TAKAHASHI Yoshihiro
- Department of Applied Physics, Tohoku University
-
- MIYAZAKI Takamichi
- Department of Instrumental Analysis, Tohoku University
-
- TERAKADO Nobuaki
- Department of Applied Physics, Tohoku University
-
- ONOUE Noriko
- Department of Cardiovascular Medicine, National Hospital Organization, Sendai Medical Center
-
- SHINOZAKI Tsuyoshi
- Department of Cardiovascular Medicine, National Hospital Organization, Sendai Medical Center
-
- FUJIWARA Takumi
- Department of Applied Physics, Tohoku University
抄録
We prepared a borosilicate glass, in which the ZrO2 phase is singly crystallizable, i.e., 15Na2O–15ZrO2–30B2O3–40SiO2 glass, and investigated the texture and morphology of the resulting glass-ceramics. ZrO2 dendrites with a tetragonal system (high-temperature phase) were developed as initial phase, and the tetragonal phase was transformed to the monoclinic phase (low-temperature phase) by elongation of the heat-treatment time, and finally the needle-/rod-like crystals on a scale of few hundred nanometers were obtained. The glass-ceramics with monoclinic ZrO2 showed photoluminescence around 480 nm by excitation in the ultraviolet region. The effect of TiO2-addition on the photoluminescent property was also considered.
収録刊行物
-
- Journal of the Ceramic Society of Japan
-
Journal of the Ceramic Society of Japan 125 (4), 343-347, 2017
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205285912064
-
- NII論文ID
- 130005530336
-
- ISSN
- 13486535
- 18820743
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可