Morphology Evolution of γ' Precipitates during Isothermal Exposure in Wrought Ni-Based Superalloy Inconel X-750
-
- Hisazawa Hiromu
- Department of Materials Science and Engineering, Interdisciplinary Graduate School of Science and Engineering, Tokyo Institute of Technology
-
- Terada Yoshihiro
- Department of Materials Science and Engineering, School of Materials and Chemical Technology, Tokyo Institute of Technology
-
- Takeyama Masao
- Department of Materials Science and Engineering, School of Materials and Chemical Technology, Tokyo Institute of Technology
書誌事項
- タイトル別名
-
- Morphology Evolution of γ′ Precipitates during Isothermal Exposure in Wrought Ni-Based Superalloy Inconel X-750
この論文をさがす
抄録
<p>The morphological evolution of γ′ precipitates and lattice misfit with isothermal aging were closely investigated in wrought Ni-based superalloy Inconel X-750. The γ′ morphology dramatically changes in terms of shape, distribution, coalescence and coherency at the γ/γ′ interface. These processes and their dependence on temperature are summarized as a γ′ morphology map together with a time–temperature–precipitation (TTP) diagram through quantifying relevant morphological parameters. The lattice misfit was measured by X-ray diffraction and is positive; it decreases from 0.6% at room temperature to 0.1% at the aging temperature. These results suggest that the morphological changes of the γ′ precipitates are attributable to very low lattice misfit, the interaction of the elastic field, the volume fraction of the precipitates and incoherence in γ/γ′ interface.</p>
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 58 (5), 817-824, 2017
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679231287552
-
- NII論文ID
- 130005611961
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 028138049
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- IRDB
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可