書誌事項
- タイトル別名
-
- Morphology of Cu Particle during High-Temperature Deformation in Cu-added Ferritic Stainless Steels
- Cu テンカ フェライトケイ ステンレスコウ ノ コウオン ヘンケイ チュウ ノ Cu リュウシ ケイタイ
この論文をさがす
抄録
<p>In this study, Cu-added ferritic stainless steel sheets were investigated to understand the influences of Cu contents on the high-temperature strength during the high-temperature deformation. High-temperature proof stress at 700~900°C was improved greatly by addition of more than 1% of Cu. In the case of static aging at 900°C, the rod-shaped ε-Cu particles satisfied the K-S orientation relationship with the α matrix, but spherical-shaped ε-Cu particles without specific orientation relationship started appearing during the tensile deformation at 900°C. Similarly, the spherical-shaped and fine ε-Cu particles were observed during the thermal fatigue process in the temperature range from 200°C to 700°C with a 50% restriction ratio. During the observation using the high-temperature in-situ TEM straining, it was clarified that the ε-Cu particles were divided by dislocation shearing and parts of them were found dissolved. According to the LSW theory, it was suggested that the microstructure with fine and spherical-shaped ε-Cu particles was formed by the repetition of dissolution and precipitation during the high-temperature deformation.</p>
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 103 (9), 539-548, 2017
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205217760384
-
- NII論文ID
- 130006029644
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
-
- NDL書誌ID
- 028520422
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可