POFA-Engineered Alkali-activated Cementitious Composite Performance in Acid Environment
-
- Salami Babatunde Abiodun
- School of Civil Engineering, Universiti Sains Malaysia, Engineering Campus, Pulau Pinang, Malaysia.
-
- Johari Megat Azmi Megat
- School of Civil Engineering, Universiti Sains Malaysia, Engineering Campus, Pulau Pinang, Malaysia.
-
- Ahmad Zainal Arifin
- School of Materials and Mineral Resources Engineering, Universiti Sains Malaysia, Engineering Campus, Pulau Pinang, Malaysia.
-
- Maslehuddin Mohammed
- Center for Engineering Research, Research Institute, King Fahd University of Petroleum and Minerals, Dhahran, Saudi Arabia.
抄録
<p>The durability performance of palm oil fuel ash engineered alkali-activated cementitious composite (POFA-EACC) mortar exposed to different acid solutions is assessed in this study. 50 mm cubic specimens used for the study were prepared from 100% POFA, alkali-activator (Na2SiO3(aq)/NaOH(aq)) ratios of 2.5, different molarities (10, 12 and 14 M) of NaOH(aq) and 2% volume fraction of polyvinyl alcohol (PVA) fibres. Specimens were exposed to 10% H2SO4(aq), 10% HNO3(aq) and 10% HCl(aq) at pH of 0.56, 0.52 and 0.42 respectively for 3, 6 and 9 months, with unexposed specimens as control. Small changes in compressive strength were identified with POFA mortar specimens during exposure to H2SO4(aq), while exposure to HNO3(aq) and HCl(aq) greatly reduced the strength of the POFA mortar specimens. The results were supported through microstructural examinations using SEM, while the characterization was done using XRD and FTIR. The high resistance of POFA-EACC mortar to H2SO4(aq) is the contribution received through the formation of gypsum, which hinders the infiltration of more acids into the matrix microstructure.</p>
収録刊行物
-
- Journal of Advanced Concrete Technology
-
Journal of Advanced Concrete Technology 15 (11), 684-699, 2017-11-23
公益社団法人 日本コンクリート工学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680195607424
-
- NII論文ID
- 130006216884
-
- ISSN
- 13473913
- 13468014
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可