- Modeling of criteria on prevention of sensitization by delta-ferrite in austenitic stainless steel weld metal
- -オーステナイト系ステンレス鋼溶接金属の鋭敏化挙動のモデル化-
- - Modeling of sensitization in austenitic stainless steel weld metal -
抄録
The prevention of sensitization by delta-ferrite in austenitic stainless steel weld metal was investigated from a point of view of the required fraction of delta-ferrite to prevent in weld metal containing not low carbon. Intergranular corrosion test in copper-copper sulfate solution was conducted using the 20%Cr-11/14%Ni-0.045/0.075%C weld metal after sensitizing treatment at 650°C for 3h. The intergranular corrosion was prevented in the weld metal containing sufficiently high fraction of delta ferrite even in case of high carbon content such as 0.06%. A physical model was suggested to determine the delta-ferrite necessary for each carbon content in weld metal. This model was founded on the concept that sufficient fraction of delta ferrite exhausts those carbon atoms in austenitic phase due to consumption by rapid growth of chromium carbide in delta ferrite. It was confirmed the required fraction of delta ferrite to prevent the sensitization in each carbon content agrees with that of experimental results.
収録刊行物
-
- 溶接学会論文集
-
溶接学会論文集 35 (4), 141-148, 2017
一般社団法人 溶接学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679702220800
-
- NII論文ID
- 130006243226
-
- ISSN
- 24348252
- 02884771
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可