レーザ予熱方式を用いた中炭素鋼の摩擦攪拌接合

DOI Web Site Web Site 参考文献20件

書誌事項

タイトル別名
  • Friction Stir Welding of Medium Carbon Steel with Laser-Preheating
  • レーザ ヨネツ ホウシキ オ モチイタ チュウ タンソコウ ノ マサツ カクハン セツゴウ

この論文をさがす

抄録

<p>Friction Stir Welding (FSW) has expanded to many metallic materials with higher melting points or much higher strength than the aluminum alloys. If the tool travels too quickly along the welding seam during the welding process or if the melting point of the workpiece is high, the frictional heat generated between the tool and the workpiece may not be sufficient to cause material flow. Insufficient heat input results in the formation of groove or tunnel-shaped defects in the stir zone and also severe wear or breaking of the FSW tool. To solve these problems, a higher heat input is required to soften the materials. Therefore, several preheating methods have been adopted to increase the heat input. In this study, a fiber laser was used as the preheating source during the FSW. In this experiment, the effect of the laser-preheating on the defect formation and tool rotational torque during the FSW was investigated. Additionally, a difference in the material flow during the conventional FSW and laser-preheating FSW was observed by two pairs of x-ray transmission real-time imaging systems. As a result, it was found that the laser preheating reduced the defect formation and the tool rotational torque during the FSW. Furthermore, laser beam irradiation on the retreating side (RS) was the most effective in reducing the defect formation. On the other hand, the irradiation on the advancing side (AS) was the most effective in reducing the tool rotational torque.</p>

収録刊行物

  • 鉄と鋼

    鉄と鋼 104 (7), 369-376, 2018

    一般社団法人 日本鉄鋼協会

参考文献 (20)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ