- Fracture strength for precision processed dental ceramics
抄録
<p>Dental ceramics are affected by milling process of CAM machine, and these surfaces are caused micro-cracks. This problem leads to cause severe fracture and reduce the fatigue life. The aim of this study is to eliminate the micro-crack of dental ceramics surface by using micro slurry-jet (MSJ) process. MSJ is a blasting technique that uses fine particles as the abrasive media, along with compressed air and pure water. In this study, CERASMART 270 that is composite resin ceramics was used as a specimen. The surface of specimens was adjusted MSJ process after polishing with #1500 sandpaper and dental abrasive. The MSJ processed and polished surfaces were observed using a laser microscopy to examined residual defects and micro-cracks. As a result, it was found that residual defects and micro-cracks on the surface after polishing could be able to expose and eliminate. This study showed that MSJ process is an effective technique for eliminating residual defects and micro-cracks on the surface of dental ceramics.</p>
収録刊行物
-
- 年次大会
-
年次大会 2018 (0), J0220203-, 2018
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390845713069243008
-
- NII論文ID
- 130007619255
-
- ISSN
- 24242667
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可