- Influence of Quenching Temperature on Impact-wear Resistance of 27%Cr Cast Iron
- 27%Cr チュウテツ ノ タイショウゲキ マモウ ニ オヨボス ヤキイレ オンド ノ エイキョウ
この論文をさがす
抄録
<p> It has already been reported that the use of a chiller which suppresses the occurrence of internal casting defects in cast products of 27%Cr cast iron results in the deterioration of impact-wear resistance in the as cast state. In this paper, impact-wear behavior of 27%Cr cast iron was investigated after quenching at various temperatures to improve the impact wear resistance. Evaluation of impact-wear resistance was based on wear loss and decrease of thickness using air blasting machine. Microstructural analysis was performed using a scanning electron microscope with energy dispersive X-ray spectrometer, X-ray diffractometer and ferrite meter. Quenching at temperatures over 1323K results in improved impact wear resistance, as compared with the as cast state. Below that temperature, impact-wear becomes severe. This can be explained by the change in the volume fraction of retained austenite and martensite in the matrix and the self-temper softening of martensite caused by the generation of impingement heat between abrasive media and experimental samples.</p>
収録刊行物
-
- 鋳造工学
-
鋳造工学 93 (1), 11-19, 2021-01-25
公益社団法人 日本鋳造工学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1391412881287473536
-
- NII論文ID
- 130007979316
-
- NII書誌ID
- AN10514770
-
- ISSN
- 21855374
- 13420429
-
- NDL書誌ID
- 031240984
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- CiNii Articles
- Crossref
-
- 抄録ライセンスフラグ
- 使用不可