希土類‐アルカリ金属系Ｍ型フェライトの合成と磁気的性質

• 村上 亮

  東北大学工学部材料物性学科

• 嶋 邦弘

  田中貴金属工業(株)

• 高村 仁

  東北大学工学部材料物性学科

• 田中 煕巳

  東北大学工学部材料物性学科

• 岡田 益男

  東北大学工学部材料物性学科

書誌事項

タイトル別名

• Synthesis and Magnetic Properties of Rare Earth-Alkaline Metal M-Type Ferrites.

抄録

The apparent phases and magnetic properties of ferrites of the RE₂O₃-AM₂O-Fe₂O₃ system (RE=Y, La, Ce, Pr, Nd, Sm, Gd, and AM=Na, K, Rb) were studied. The observed phases were classified according to the combination of rare earth metal and alkaline metal. M-type ferrites, which have a magnetoplumbite structure, were obtained in the La₂O₃AM₂O-Fe₂O₃system (AM=Na, K, Rb). M-type ferrites were synthesized at over 1473 K for the La-Na system, 1573 K for the La-K system, and 1673 K for the La-Rb system. A single phase of M-type ferrite was prepared in (La_1-xK_x)O·6Fe ₂O₃ at x=0.2. The magnetization of (La_0.8K_0.2)O·6Fe₂O₃ is 86μWb·m·kg^-1,and the Curie temperature is 708 K.

収録刊行物

• 日本応用磁気学会誌

  日本応用磁気学会誌 20 (2), 213-216, 1996

  公益社団法人 日本磁気学会

キーワード

• rare earth metal
• alkaline metal
• M-type ferrites
• single phase
• (La_0.8K_0.2)O· 6Fe₂O₃

詳細情報

• CRID: 1390282680070062720
• NII論文ID: 20000345848
• NII書誌ID: AN0031390X
• DOI: 10.3379/jmsjmag.20.213
• COI: 1:CAS:528:DyaK28XivFChtL8%3D
• ISSN: 18804004
• ISSN: 02850192
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可