- Magnetoresistance and Magnetism in CoxCu100-x Alloys Produced by Mechanical Alloying.
この論文をさがす
抄録
CoxCu100-x (x= 10-30) alloys were prepared by mechanically milling mixtures of elemental Co and Cu powders. The structure, magnetoresistance (MR), and magnetic properties were examined for the as-milled and annealed alloys. The hcp-Co phase disappeared after milling for 50 h, and the Co atoms were dissolved in the fcc-Cu phase. The MR ratio showed a maximum of 6.7% (15 kOe, room temperature) at a Co concentration of x = 20. For higher Co concentrations, the annealing temperature needed to produce high magnetoresistance was lower and the annealing time was shorter. The CoxCu100-x alloy with x=20 showing a maximum MR exhibited superparamagnetic behavior, but had a slight ferromagnetic state. The average grain size of Co particles, estimated from the temperature dependence of magnetization, was 5-7 nm.
収録刊行物
-
- 日本応用磁気学会誌
-
日本応用磁気学会誌 20 (2), 381-384, 1996
公益社団法人 日本磁気学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680070001920
-
- NII論文ID
- 20000346270
-
- NII書誌ID
- AN0031390X
-
- COI
- 1:CAS:528:DyaK28XivFCgsr0%3D
-
- ISSN
- 18804004
- 02850192
- http://id.crossref.org/issn/02850192
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可