Joint resurfacing using allograft chondrocytes and synthetic biodegradable polymer scaffolds
抄録
<jats:title>Abstract</jats:title><jats:p>Cartilage implants which could potentially be used to resurface damaged joints were created using rabbit articular chondrocytes and synthetic, biodegradable polymer scaffolds. Cells were serially passaged and then cultured <jats:italic>in vivo</jats:italic> on fibrous polyglycolic acid (PGA) scaffolds. Cell‐PGA constructs were implanted <jats:italic>in vivo</jats:italic> as allografts to repair 3‐mm diameter, full thickness defects in the knee joints of adult rabbits, and cartilage repair was assessed histologically over 6 months. <jats:italic>In vitro</jats:italic>, chondrocytes proliferated on PGA and regenerated cartilaginous matrix. Collagen and glycosaminoglycan (GAG) represented 20 to 8% of the implant dry weight (dw), respectively, at the time of <jats:italic>in vivo</jats:italic> implantation; the remainder was PGA and unspecified components. Implants based on passaged chondrocytes had 1.7‐times as much GAG and 2.6‐times as much collagen as those based on primary chondrocytes. <jats:italic>In vivo</jats:italic>, cartilaginous repair tissue was observed after implantation of PGA both with and without cultured chondrocytes. Six month repair was qualitatively better for cell‐PGA allografts than for PGA alone, with respect to: (1) surface smoothness, (2) columnar alignment of chondrocytes, (3) spatially uniform GAG distribution, (4) reconstitution of the subchondral plate, and (5) bonding of the repair tissue to the underlying bone. These pilot studies demonstrate that it is feasible to use cell‐polymer allografts for joint resurfacing <jats:italic>in vivo</jats:italic>. © 1994 John Wiley & Sons, Inc.</jats:p>
収録刊行物
-
- Journal of Biomedical Materials Research
-
Journal of Biomedical Materials Research 28 (8), 891-899, 1994-08
Wiley
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1362544421086984960
-
- NII論文ID
- 30002072812
-
- ISSN
- 10974636
- 00219304
- http://id.crossref.org/issn/00219304
-
- データソース種別
-
- Crossref
- CiNii Articles