Investigation of the Thermal Dissociation, Reassociation, and Synthesis of Zircon

• C. E. CURTIS

• H. G. SOWMAN

抄録

The amount of dissociation present in zircon after 2‐hour heating periods at temperatures between 2800° and 3600°F. was determined by X‐ray analysis of quenched specimens. The course of dissociation was followed in the same manner during 8‐ to 10‐hour heating periods at temperatures of 2800°, 3000°, and 3200°F., respectively. Data are included that pertain to the synthesis of zircon from its constituent oxides at temperatures from 2100° to 2800°F. The results indicate that zircon is the stable phase up to about 2800°F.; above that temperature it becomes unstable, the degree of instability increasing with temperature, especially above 3200°F. On the basis of the results obtained from this investigation, a revision of the present phase diagram of the system zirconia–silica is proposed.

収録刊行物

• Journal of the American Ceramic Society

  Journal of the American Ceramic Society 36 (6), 190-198, 1953-06

  Wiley

キーワード

• Materials Chemistry
• Ceramics and Composites

詳細情報

• CRID: 1360011145372392320
• NII論文ID: 30015549452
• DOI: 10.1111/j.1151-2916.1953.tb12865.x
• ISSN: 15512916
• ISSN: 00027820
• Web Site: https://api.wiley.com/onlinelibrary/tdm/v1/articles/10.1111%2Fj.1151-2916.1953.tb12865.x
• Web Site: http://onlinelibrary.wiley.com/wol1/doi/10.1111/j.1151-2916.1953.tb12865.x/fullpdf
• データソース種別:
  • Crossref
  • CiNii Articles