Improvement in Thermoelectric Characteristics of n‐type Iron Disilicide by Local Composition Modification
抄録
<jats:p>High thermoelectric figure of merit semiconducting ceramics of <jats:italic>n</jats:italic>‐type iron disilicide with modified local compositions have been developed. Sintering and annealing of the composite powder composed of iron disilicide and precipitated cobalt (II) hydroxide resulted in the dissolution of excess Co and oxygen into the iron disilicide phase. Excess Co segregated to the grain boundary region, while interstitially incorporated oxygen was distributed homogeneously in the microstructure. The maximum figure of merit achieved was 5.2 × 10<jats:sup>−4</jats:sup>/K at 673 K.</jats:p>
収録刊行物
-
- Journal of the American Ceramic Society
-
Journal of the American Ceramic Society 78 (4), 1089-1092, 1995-04