- M. Sherif El-Eskandarany
- Institute for Materials Research, Tohoku University, Sendai 980, Japan
-
- K. Aoki
- Institute for Materials Research, Tohoku University, Sendai 980, Japan
-
- K. Suzuki
- Institute for Materials Research, Tohoku University, Sendai 980, Japan
抄録
<jats:p>Aluminum tantalum nitride amorphous alloy powders have been synthesized by a high energy ball mill under purified nitrogen gas (N2) flow at room temperature. The alloy powders were characterized by means of transmission electron microscopy, differential thermal analysis, and chemical analysis. An amorphous phase containing 18 at. % N2 was obtained after 65 ks of the milling time. At the final stage of milling (72 ks) the crystallization temperature, Tx, and enthalpy change of crystallization, ΔHx, are 1115 K and −95 kJ mol−1, respectively.</jats:p>
収録刊行物
-
- Applied Physics Letters
-
Applied Physics Letters 60 (13), 1562-1563, 1992-03-30
AIP Publishing
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1361137045088889088
-
- NII論文ID
- 30015759937
-
- DOI
- 10.1063/1.107251
-
- ISSN
- 10773118
- 00036951
-
- データソース種別
-
- Crossref
- CiNii Articles