Morphological and structural evolutions of nonequilibrium titanium-nitride alloy powders produced by reactive ball milling
抄録
<jats:p>Nonequilibrium titanium-nitride alloy powders have been fabricated by a high energetic ball mill under nitrogen gas flow at room temperature and characterized by means of x-ray diffraction, scanning electron microscopy, transmission electron microscopy, and differential scanning calorimetry. Initial hcp titanium is completely transformed to nonequilibrium-fcc Ti–N after 720 ks of the milling time. The fcc Ti–N phase is stable at relatively low temperature and transforms at 855 K to Ti<jats:sub>2</jats:sub>N and δ phases. At the final stage of milling, the particle- and grain-sizes of alloy powders are 1 mm and 5 nm, respectively, and the lattice parameter is 0.419 nm.</jats:p>
収録刊行物
-
- Journal of Materials Research
-
Journal of Materials Research 7 (4), 888-893, 1992-04
Springer Science and Business Media LLC
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1361418518500350720
-
- NII論文ID
- 30029696581
-
- ISSN
- 20445326
- 08842914
- http://id.crossref.org/issn/08842914
-
- データソース種別
-
- Crossref
- CiNii Articles