- Formation of FeSi<SUB>2</SUB> from Sintered FeSi-Fe<SUB>2</SUB>Si<SUB>5</SUB> Eutectic Alloy
- FeSi-Fe2Si5共晶合金の焼結体から生成されるFeSi2について
- FeSi Fe2Si5キョウショウ ゴウキン ノ ショウケツタイ カラ セイセ
この論文をさがす
抄録
The phase transformation from a sintered eutectic alloy consisting of ε-FeSi and α-Fe2Si5 to β-FeSi2 has been studied by metallographic observations, by X-ray quantitative analysis techniques, and by measuring the resistivity and thermoelectric power corresponding to various annealing temperatures and times. It is found that the resistivity increases with increasing amount of β-FeSi2 and two maximum values occur at 1123 and 1133 K in the relationship between the resistivity and the annealing temperature. A drastic decrease in the resistivity can be also confirmed in the temperature range from 1123 to 1133 K. Two different reactions separately occur in the regions below 1123 and above 1133 K. Below 1123 K β-FeSi2 is formed mainly by the decomposition reaction, α→β+Si, and followed by the subsidiary reaction, Si+ε→β; above 1133 K β-FeSi2 is produced by the peritectoid reaction, ε+α→β. In the former reaction, the complete β-FeSi2 is obtained by an effective annealing at 1113 K for 3.6×104 s.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 48 (8), 843-847, 1984
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681462590080
-
- NII論文ID
- 130007339803
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 2997553
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可