- Temperature Range of Formation of Athermal ω Phase in Quenched β Ti-Nb Alloys
- ヤキイレ ベータ Ti Nb ゴウキン ニ オケル athermal オメガソ
- Temperature Range of Formation of Athermal ω Phase in Quenched β Ti-Nb Alloys
この論文をさがす
抄録
Negative temperature dependence (NTD) of electrical resistivity (ρ) was investigated on several Ti-Nb alloys quenched from 1073 K in relation to α″ martensite and athermal ω phases.<BR>The estimation of starting and ending temperatures of the athermal ω formation, ωs and ωf, respectively, was attempted with special care to avoid the reverse transformation of the α″ phase and the decomposition of the retained β phase.<BR>The α″ was observed in the 20∼35%Nb alloys, and in the alloys with more than 40%Nb only the retained β was observed. The NTD was observed only in the 40%Nb alloy, and both a maximum and a minimum of ρ appeared in the temperature range of 77∼350 K. This supports the previously proposed model for the resistivity change during the athermal ω formation.<BR>The values of ωs and ωf estimated from resistivity temperature curves decreased with Nb content. The composition range of alloys, in which the so-called quenched ω phase was observed, coincided with that of the alloys which was intermediate between ωs and ωf at room temperature.<BR>Therefore, the “quenched ω” may be the athermal ω with a large volume fraction at room temperature.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 52 (12), 1206-1211, 1988
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206484276992
-
- NII論文ID
- 130007336948
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
- http://id.crossref.org/issn/00214426
- http://id.crossref.org/issn/00214876
-
- NDL書誌ID
- 3209742
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可