The Influence of Graphitic Structure of Carbon Electrode on Aging Behavior of Electric Double Layer Capacitor
-
- TOKITA Masahiro
- Graduate School of Science and Engineering, Yamaguchi University
-
- EGASHIRA Minato
- Graduate School of Science and Engineering, Yamaguchi University
-
- YOSHIMOTO Nobuko
- Graduate School of Science and Engineering, Yamaguchi University
-
- MORITA Masayuki
- Graduate School of Science and Engineering, Yamaguchi University
この論文をさがす
抄録
The double-layer capacitors and their degradation after aging process for nano-fibrous carbon electrodes with various graphitic structures have been compared. The nano-fibrous carbon with amorphous structure has successfully been prepared from biomass precursor. The nano-fibrous carbons with graphitic and amorphous structures exhibit similar specific surface area and double-layer capacitance. However, the change of the capacitances of the cells consisting of both carbons by the aging process under high temperature and high voltage condition are different. The amorphous nano-fibrous carbon electrode provides capacitance decrease by the deposit on electrode, while the graphitic nano-fiber provides capacitance increased likely due to the gas evolution.
収録刊行物
-
- Electrochemistry
-
Electrochemistry 80 (10), 752-754, 2012
公益社団法人 電気化学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206495055232
-
- NII論文ID
- 130002147491
-
- NII書誌ID
- AN00151637
-
- COI
- 1:CAS:528:DC%2BC38XhsFGlu73I
-
- ISSN
- 21862451
- 13443542
-
- NDL書誌ID
- 023980603
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用可