Effect of Homogenization Treatment on the Microstructure and Mechanical Property Evolutions of As-Cast Al–Cu Alloy during High-Pressure Torsion
-
- Abd El Aal Mohamed Ibrahim
- Mechanical Design and Production Department, Faculty of Engineering, Zagazig University Department of Material Science and Engineering, Pohang University of Science and Technology (POSTECH)
-
- Um Ho Yong
- Department of Material Science and Engineering, Pohang University of Science and Technology (POSTECH)
-
- Choi Kang Hyun
- Department of Material Science and Engineering, Pohang University of Science and Technology (POSTECH)
-
- Kim Hyoung Seop
- Department of Material Science and Engineering, Pohang University of Science and Technology (POSTECH)
書誌事項
- タイトル別名
-
- Effect of Homogenization Treatment on the Microstructure and Mechanical Property Evolutions of As-Cast Al–Cu Alloy during High-Pressure Torsion
この論文をさがす
抄録
As-cast and homogenization treated as-cast Al–Cu (3 mass% Cu) alloy samples were processed via high-pressure torsion (HPT) under an applied pressure of 8 GPa with 5 revolutions at room temperature. Microstructure, mechanical properties, and fracture surface morphology of the HPT-processed Al–Cu were investigated, demonstrating that the HPT process successfully resulted in distinct grain refinements in both samples. Significant improvements in the microhardness, tensile properties, and deformation homogeneity due to fine grains, high grain boundary misorientation angle, and homogeneous distribution of the θ phase were achieved after the HPT process of the homogenized sample. The homogenization treatment of the as-cast Al–Cu has a significant effect on the fracture surface morphology and fracture mode of the HPT-processed samples.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 55 (9), 1405-1413, 2014
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679229769088
-
- NII論文ID
- 130004455364
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 025747185
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可