Development of Nanoporous Copper Foams by Chemical Dealloying of Mechanically Alloyed Al–Cu Compounds
-
- Nam Seungjin
- School of Advanced Materials Engineering, Kookmin University
-
- Jo Hyungyung
- School of Advanced Materials Engineering, Kookmin University
-
- Choe Heeman
- School of Advanced Materials Engineering, Kookmin University
-
- Ahn Donghwan
- School of Advanced Materials Engineering, Kookmin University
-
- Choi Hyunjoo
- School of Advanced Materials Engineering, Kookmin University
書誌事項
- タイトル別名
-
- Development of Nanoporous Copper Foams by Chemical Dealloying of Mechanically Alloyed Al–Cu Compounds
この論文をさがす
抄録
We developed open-cell copper foams with uniformly distributed nanopores by chemical dealloying of Al2Cu samples that were synthesized by a powder process. High-energy ball-milling was utilized for mechanical alloying of aluminum and copper powders and either hot rolling or hot pressing was then employed to consolidate the ball-milled powders into sheets or pellets. Subsequent dealloying aluminum from the samples produced nanoporous copper foams. X-ray diffractometry and scanning electron microscopy confirmed the uniform formation of Al2Cu and aluminum phases prior to dealloying, and the introduction of nanoporous structures after dealloying.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 55 (9), 1414-1418, 2014
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679229770368
-
- NII論文ID
- 130004678144
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 025747201
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可