The Effects of Fe₂P and Fe₃P Intermediate Equilibrium Phases on Glass-Forming Ability of Fe₇₆Si₉B₁₀P₅ Bulk Metallic Glass
-
- Takeuchi Akira
- Institute for Materials Research, Tohoku University
-
- Makino Akihiro
- Institute for Materials Research, Tohoku University
書誌事項
- タイトル別名
-
- The Effects of Fe<sub>2</sub>P and Fe<sub>3</sub>P Intermediate Equilibrium Phases on Glass-Forming Ability of Fe<sub>76</sub>Si<sub>9</sub>B<sub>10</sub>P<sub>5</sub> Bulk Metallic Glass
この論文をさがす
抄録
The glass-forming ability (GFA) of an Fe76Si9B10P5 bulk metallic glass (BMG) was evaluated thermodynamically with commercial software, Thermo-Calc, with Fe-base database, TCFE7 by utilizing its best ability to deal with equilibrium phases. The Fe76Si9B10P5 BMG was selected because it is the simplest Fe-rich BMG belonging to Fe-metalloid type with the greatest sample dimensions. A possible reason for the presence of intermediate equilibrium phases to degrade GFA of the Fe76Si9B10P5 was discussed. The results revealed that the Fe76Si9B10P5 BMG is characterized by near eutectic composition in the Fe-rich Fe-Si-B-P quaternary system and by the simultaneous presence of Fe3P and absence of Fe2B phases in equilibrium at a range below the solidus- to the glass-transition temperatures. The analysis of Fe76(Si,B,P)24 alloys for equilibrium phases revealed that the Fe2P phase can degrade GFA of the Fe76Si9B10P5 BMG.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 55 (10), 1575-1581, 2014
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204252288000
-
- NII論文ID
- 130004687500
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 025805256
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可