Prediction of Intermetallic Compound Formation Sequences in Pseudo Binary Diffusion Couples : Experimental Examinations for (Sn-xZn)/Cu (x = 2, 5, 10, 15, 20 and 25 mass%) by a Kinetic Model with Thermodynamic Data Using MDR Diagram
-
- Terashima Shinichi
- Advanced Technology Research Laboratories, Nippon Steel & Sumitomo Metal Corporation
-
- Sasaki Tsutomu
- Technical Planning Department, Nippon Steel & Sumitomo Metal Corporation
書誌事項
- タイトル別名
-
- Prediction of Intermetallic Compound Formation Sequences in Pseudo Binary Diffusion Couples: Experimental Examinations for (Sn-<i>x</i>Zn)/Cu (<i>x</i> = 2, 5, 10, 15, 20 and 25 mass%) by a Kinetic Model with Thermodynamic Data Using MDR Diagram
この論文をさがす
抄録
A kinetic model based on the principle of maximum degradation rate of the total system free energy, MDR law, using thermodynamic data is applied to (Sn-Zn)/Cu diffusion couples to predict intermetallic compound phases and their order to be formed. According to this model, only γ-Cu5Zn8 is predicted to appear when Zn content is less than 10 mass%, while both γ-Cu5Zn8 and ε-CuZn4 can exist with 10 mass%Zn or more, which was in a good agreement with EPMA and TEM observations of Cu plates dipped into Sn-Zn baths. Therefore, it is concluded that the phase prediction based on the MDR law can also be applied to pseudo binary diffusion systems.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 55 (11), 1750-1754, 2014
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204252182144
-
- NII論文ID
- 130004691006
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 025890797
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可