書誌事項
- タイトル別名
-
- Tensile Characteristics of High-Cr-Fraction Cr-Cu Composite at Various Temperatures
- コウハイゴウリツ Cr-Cu フクゴウザイ ノ ヒッパリ トクセイ ニ オケル オンド イソンセイ
この論文をさがす
抄録
In order to gain the fundamental knowledge of plastic deformability in a Cr-Cu composite material containing a high fraction of Cr particles, tensile tests of 50mass%Cr-Cu composites were performed at 299K to 473K. Although single-phase Cr generally shows brittle fracture at temperatures lower than approximately 350K, the Cr-Cu composite shows ductile fracture at all tested temperatures. The tensile strength and fracture elongation decreased with increasing testing temperature. These tensile properties of the high-Cr-fraction Cr-Cu composite originate from the properties of a matrix material comprising a Cu alloy with a small amount of dissolved and precipitated Cr. However, the reduction in area was increased with increasing testing temperature. The deformation characteristics of the Cr-Cu composites were considered in terms of the re-arrangement, elongation, and rotation of Cr particles in a ductile Cu matrix. In addition, the ductile-brittle transition behavior of Cr particles would affect the tensile property of Cr-Cu composite at 353K to 373K, which is the range of the ductile-brittle transition temperature (DBTT).
収録刊行物
-
- 塑性と加工
-
塑性と加工 56 (648), 34-39, 2015
一般社団法人 日本塑性加工学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681476344192
-
- NII論文ID
- 130004787568
-
- NII書誌ID
- AN00135062
-
- ISSN
- 18820166
- 00381586
-
- NDL書誌ID
- 026051164
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可