- Effect of Electroless Ni-P Plating on the Mechanical Properties of Al-4%Ge Alloy
- Al-4%Ge ゴウキン ノ キカイテキ セイシツ ニ オヨボス ムデンカイ ニッケル-リンメッキ ノ エイキョウ
この論文をさがす
抄録
In this study, the effect of electroless Ni-P plating on the mechanical properties of Al-4%Ge alloy was investigated. As the results, the following points were clarified. (1) Tensile strength of the specimen subjected to the Ni-P plating after aging treatment or furnace cooling treatment was improved by about 10% in comparison to one of the non-processed specimens. (2) Breaking elongation of the specimen subjected to the Ni-P plating after aging treatment showed no significant changes in comparison to one of the non-processed specimens. On the other hand, breaking elongation of the specimen subjected to Ni-P plating after a furnace cooling treatment was reduced to 70% in comparison to one of the non-processed specimens. (3) Fatigue strength of the specimen subjected to the Ni-P plating after a furnace cooling treatment was overall reduced rather than one of non-processed specimens. (4) Fatigue strength of the specimen subjected to the Ni-P plating after aging treatment was overall reduced, except for the low-stress region, rather than one of the non-processed specimens. (5) In the specimen subjected to Ni-P plating after a furnace cooling treatment or aging treatment, clear hydrogen desorption was recognized. On the other hand, there was only hydrogen desorption from a few of the non-processed specimens.<br> Especially, it is considered that the poor fatigue strength and ductility of the plating materials are mainly due to the interaction between the surface precipitates and hydrogen gas.<br>
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 79 (3), 146-150, 2015
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681459258752
-
- NII論文ID
- 130004786485
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 026225808
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可