砂型鋳物及び連続鋳造材を素材としたオーステンパ球状黒鉛鋳鉄の切削性

DOI Web Site

書誌事項

タイトル別名
  • Machinability of Austempered Spheroidal Graphite Cast Iron made by Sand Mold and Continuous Casting Methods
  • スナガタ イモノ オヨビ レンゾク チュウゾウザイ オ ソザイ ト シタ オーステンパ キュウジョウ コクエン チュウテツ ノ セッサクセイ

この論文をさがす

抄録

<p>  In this study, the machinability of austempered spheroidal graphite cast iron made by different casting methods was investigated. Spheroidal graphite cast iron samples made by sand mold casting and continuous casting, respectively ADI-S and ADI-C, were used. From the results of cutting tests, the machinability of ADI-C was always excellent compared with that of ADI-S at cutting speeds from 100 to 365m/min. The feed and thrust forces of ADI-S were higher than those of ADI-C at high cutting speeds, although their cutting resistance was almost the same at low cutting speeds. In addition, the microstructure of ADI-S chips was found to be greatly deformed near the chip-tool interface for ADI-S compared with ADI-C. It has been reported that there always exists retained austenite in austempered spheroidal graphite cast iron, and that the retained austenite transforms to deformation-induced martensite on the machined surface when the austempered spheroidal graphite cast iron is machined. From the results of the comparative analysis of ADI-S and ADI-C, the average relative volume ratio of retained austenite increased with increasing cutting speed for both ADI-S and ADI-C, and was about double in the case of ADI-S at high cutting speeds such as 365m/min. From these results, it is clear that the retained austenite in both ADI-S and ADI-C does not transform to deformation-induced martensite at high cutting speeds, and that ADI-C can be machined at cutting temperatures and with cutting resistances lower than those necessary for ADI-S, suggesting that the machinability of ADI-C is better than ADI-S.</p>

収録刊行物

  • 鋳造工学

    鋳造工学 87 (4), 231-238, 2015

    公益社団法人 日本鋳造工学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ