Improvement of Uniform Elongation by Low Temperature Annealing in Al-2.5%Mg Alloy Processed by Accumulative Roll Bonding
-
- Kashihara Keizo
- National Institute of Technology, Wakayama College
-
- Komi Yoshikazu
- National Institute of Technology, Wakayama College
-
- Terada Daisuke
- Kyoto University
-
- Tsuji Nobuhiro
- Kyoto University
この論文をさがす
抄録
Al-2.5%Mg alloy (A5052) sheets were processed by accumulative roll bonding (ARB) for 1 to 7 cycles (equivalent strains from 0.8 to 5.6) at room temperature. The sheets processed by ARB for 7 cycles were then annealed isochronally for 30 min at temperatures in the range from 100°C to 400°C. Interestingly, it was found that the specimen annealed at 200°C followed by 7 cycles of ARB had the same level of yield stress (about 320 MPa) but a larger uniform elongation than the specimen processed by 3 cycles of ARB. The improvement in uniform elongation by low-temperature annealing is discussed in terms of the mechanism that the evolution of dislocation substructures inside ultra-fine grains causes plastic instability at a very early stage of the tensile test. Hardening by annealing was also observed in the specimen annealed at 100°C followed by 7 cycles of ARB.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 56 (6), 803-807, 2015
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204252720128
-
- NII論文ID
- 40020473901
- 130005072151
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 026412745
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可