Effects of Si on Tensile Properties Associated with Deformation-Induced ε-Martensitic Transformation in High Mn Austenitic Alloys
-
- Koyama Motomichi
- Kyushu University
-
- Sawaguchi Takahiro
- National Institute for Materials Science
-
- Tsuzaki Kaneaki
- Kyushu University National Institute for Materials Science
書誌事項
- タイトル別名
-
- Effects of Si on Tensile Properties Associated with Deformation-Induced ε-Martensitic Transformation in High Mn Austenitic Alloys
この論文をさがす
抄録
We investigated the effect of Si on the tensile properties of Fe-33Mn, Fe-33Mn-4Si, and Fe-33Mn-6Si austenitic alloys (mass%) at 273, 294, 323, and 423 K. The Si addition promoted the deformation-induced ε-martensitic transformation, thereby enhancing the work-hardening capacity. In terms of Considère’s criterion, the enhanced work-hardening capacity can improve uniform elongation. However, the Si addition simultaneously promoted brittle cracking associated with ε-martensite, tending toward decreasing elongation. As a result of the ambivalent roles of Si related to ε-martensite, the elongation–strength balance was improved by the addition of 4%Si, but was deteriorated when the Si content increased to 6%. As an additional effect, the Si addition changed the microvoid-formation behavior, resulting in decreasing local elongations.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 56 (6), 819-825, 2015
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679229412096
-
- NII論文ID
- 40020473927
- 130005072142
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 026412776
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可