Stabillity of long-preiod stacking ordered structures at elevated temperatures examined by multicolor synchrotron radiation X-ray scattering /diffraction measurements
-
- Okuda Hiroshi
- Department of Materials Science and Engineering, Kyoto University
-
- Horiuchi Toshiki
- Department of Materials Science and Engineering, Kyoto University
-
- Tanaka Hiroto
- Department of Materials Science and Engineering, Kyoto University
-
- Yamasaki Michiaki
- Department of Materials Science and Engineering, Kumamoto University
-
- Kawamura Yoshihito
- Department of Materials Science and Engineering, Kumamoto University
-
- Kimura Shigeru
- Japan Synchrotron Radiation Research Institute, SPring8
書誌事項
- タイトル別名
-
- Stability of Long-Period Stacking Ordered Structures at Elevated Temperatures Examined by Multicolor Synchrotron Radiation X-ray Scattering/Diffraction Measurements
この論文をさがす
抄録
Stability of long-period stacking ordered (LPSO) structures of Mg-Zn-Y ternary alloys at elevated temperatures was examined by multicolor synchrotron radiation small- and medium-angle scattering/diffraction. The LPSO structures directly melted during heating, and the formation of LPSO was observed from supercooled liquid. The temperatures of complete dissolution and the onset of formation of LPSO phases were measured by monitoring the first diffraction peak of 14H, 18R and 10H compositional modulation. The stability of composition modulation in c axis direction was found to be the same as that of L12 cluster ordering in the segregation layer in both heating and cooling processes, i.e., dissolution and formation. Supercooling of LPSO was obtained for the heating/cooling rate of 10 K/min.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 56 (7), 906-909, 2015
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204253504128
-
- NII論文ID
- 130005083544
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 026564310
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可