溶液含浸法を用いたアルミナ—スピネル複合多孔体の作製

DOI Web Site 被引用文献1件 参考文献7件 オープンアクセス

書誌事項

タイトル別名
  • Fabrication of Porous Spinel-Alumina Ceramic Composite by a Solution Impregnation Method
  • 溶液含浸法を用いたアルミナースピネル複合多孔体の作製
  • ヨウエキ ガンシンホウ オ モチイタ アルミナースピネル フクゴウ タコウタイ ノ サクセイ

この論文をさがす

抄録

Porous MgAl2O4-Al2O3 ceramic composites were fabricated by impregnating porous Al2O3 bodies calcined at various temperatures with Mg(NO3)2 aqueous solution under reduced pressure, followed by firing at 1500℃. Porous Al2O3 bodies were with continuously long-ranged pore structure was prepared by a unidirectional freeze casting using aqueous slurries and then calcined at 1300℃ 1400℃. The effects of the calcination temperature of Al2O3 bodies and the number of Mg(NO3)2 impregnation on spinel formation at 1500℃ were investigated. The amount of spinel in the bodies sintered at 1500℃ increased with increasing the number of the impregnation with Mg(NO3)2 solution and decreasing calcination temperature of Al2O3 bodies. When the Al2O3 bodies calcined at 1400℃, Mg(NO3)2 solution was difficult to penetrate into Al2O3 ceramic walls because of the densification of Al2O3 ceramic walls. Thus, spinel tended to form near the Al2O3 bodies calcined at 1300℃, Mg(NO3)2 solution penetrated deeper into Al2O3 ceramic walls. And therefore, Mg widely distributed in the Al2O3 ceramic walls and a large amount of spinel formed ever at less number of the impregnation of Mg(NO3)2 solution.

収録刊行物

  • 材料

    材料 64 (6), 438-441, 2015

    公益社団法人 日本材料学会

被引用文献 (1)*注記

もっと見る

参考文献 (7)*注記

もっと見る

関連プロジェクト

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ