Magnetic Poly(Vinylsulfonic-co-Divinylbenzene) Catalysts for Direct Conversion of Cellulose into 5-Hydroxymethylfurfural Using Ionic Liquids
-
- Nguyen Trung-Dzung
- Institute of Applied Materials Science, Vietnam Academy of Science and Technology
-
- Nguyen Huy-Du
- Department of Chemistry, HCM University of Science, Vietnam National University
-
- Nguyen Phuong-Tung
- Institute of Applied Materials Science, Vietnam Academy of Science and Technology
-
- Nguyen Hoang-Duy
- Institute of Applied Materials Science, Vietnam Academy of Science and Technology Department of Chemistry, National Taiwan University
書誌事項
- タイトル別名
-
- Magnetic Poly(Vinylsulfonic-<i>co</i>-Divinylbenzene) Catalysts for Direct Conversion of Cellulose into 5-Hydroxymethylfurfural Using Ionic Liquids
この論文をさがす
抄録
Mesoporous poly(vinylsulfonic-co-divinylbenzene) (VS-DVB) and magnetic polymer (VS-DVB/CoFe2O4) are prepared and used as solid acidic catalysts to directly transform cellulose into 5-hydroxymethylfurfural (5-HMF). The characteristic and morphology of the polymers were examined by Fourier transformed infrared spectroscopy, X-ray diffraction, vibrating sample magnetometer, field-emission scanning microscope, and transmission electron microscopy. The yield of 5-HMF can reach as high as 98% from the dehydration of glucose using CrCl3·6H2O catalyst in tetrabutylammonium chloride at 120°C for 90 min. Cellulose conversion using the prepared VS-DVB in 1-butyl-3-methyl imidazolium chloride at 120°C for 180 min showed high yields of 50% glucose and 10% 5-HMF. An enhancement in 5-HMF yield was observed as reaction time increased. A combination of VS-DVB/CoFe2O4 and CrCl3·6H2O in ionic liquids was employed at optimal conditions for cellulose conversion. Magnetic catalysts were readily separated from resulting products in the magnetic field, as well as recycled and reused with negligible loss in activity. Glucose and 5-HMF yields were determined through high-performance liquid chromatography analysis.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 56 (9), 1434-1440, 2015
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679229837312
-
- NII論文ID
- 130005094784
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 026709385
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可