Ti-5Mo-3Sn 合金の機械的性質と形状記憶特性に及ぼす Zr 添加の影響

DOI Web Site Web Site 被引用文献1件 参考文献31件 オープンアクセス

書誌事項

タイトル別名
  • Effect of Zr Addition on Mechanical and Shape Memory Properties of Ti-5Mo-3Sn Alloys
  • Ti-5Mo-3Sn ゴウキン ノ キカイテキ セイシツ ト ケイジョウ キオク トクセイ ニ オヨボス Zr テンカ ノ エイキョウ

この論文をさがす

抄録

  The effects of Zr addition on the mechanical, shape memory and superelastic properties of Ti-5Mo-3Sn (mol%) based alloys were investigated with Zr content up to 24 mol%. The parent bcc phase was stabilized with increasing Zr content, and the volume fraction of the ω phase seemed independent of the Zr content. The ultimate tensile strength and fracture strain increased with increasing Zr content up to 6 mol%Zr, however, the alloy became brittle with further addition of Zr content over 8 mol%. Young's modulus was low around 37~38 GPa when Zr content was 2~6 mol%. Shape memory effect was confirmed when Zr content was less than 5 mol%, and the superelasticity appeared in 6 mol%Zr-added alloy with the good shape recovery strain of 4.3%. When the Zr addition exceeded 6 mol%, the slip deformation occurred. The slip stress was raised by Zr addition with a rate of 9.5 MPa/mol%Zr in the alloys containing 2~6 mol%Zr. It is concluded for Ti-5Mo-3Sn based alloys that Zr addition is effective to improve the mechanical properties without degradation of lattice transformation strain, and that good room-temperature superelasticity appears in the Ti-5Mo-3Sn-6Zr alloy.<br>

収録刊行物

被引用文献 (1)*注記

もっと見る

参考文献 (31)*注記

もっと見る

関連プロジェクト

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ