Effect of Zr on Microstructure and Oxidation Behavior of α and α + α₂ Ti-Al-Nb Alloys
-
- Matsunaga Sae
- Shibaura Institute of Technology High Temperature Materials Design Group, National Institute for Materials Science
-
- Serizawa Ai
- Shibaura Institute of Technology
-
- Yamabe-Mitarai Yoko
- High Temperature Materials Design Group, National Institute for Materials Science
書誌事項
- タイトル別名
-
- Effect of Zr on Microstructure and Oxidation Behavior of α and α + α<sub>2</sub> Ti-Al-Nb Alloys
- Effect of Zr on microstructure and oxidation behavior of alpha and alpha + alpha(2) Ti-Al-Nb alloys
この論文をさがす
抄録
<p>To develop high-temperature Ti alloys, microstructure and oxidation behavior were investigated in Ti-(10,15)Al-2Nb-(1,2)Zr (at%) alloys. For reference, ternary Ti-15Al-2Zr alloy was also investigated. A single α phase exists in Ti-10Al-2Nb-(1, 2)Zr alloys; on the other hand, an α and α2 two-phase was observed in Ti-15Al-2Nb-(1, 2)Zr alloys. Fine α2 precipitates of about 10 nm were observed in the Ti-15Al alloys. The oxidation behavior of Ti-Al-Nb-Zr and Ti-Al-Zr ternary alloys was investigated to understand the effect of Zr on oxidation behavior at 1023 K. It was found that Zr improves the oxidation resistance of the α phase more effectively than Nb. TiO2 was formed in all tested alloys. The addition of Zr drastically decreased the growth rate of TiO2. It was also found that the addition of Nb improved adhesion of the oxide layer.</p>
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 57 (11), 1902-1907, 2016
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204254237824
-
- NII論文ID
- 130005289954
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 027680886
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可