Fabrication of Laminated Spark Plasma Sintered Compacts Composed of Alumina-Particle-Dispersed Magnesium and Magnesium
-
- Kawamori Shigehiro
- Department of Engineering Design, Tamagawa University
-
- Fujiwara Hiroshi
- Department of Mechanical Engineering, Shizuoka Institute of Science and Technology
-
- Nagai Yoshinori
- Press Kogyo Co., Ltd.
-
- Kasuga Yukio
- Department of Engineering Design, Tamagawa University
この論文をさがす
抄録
<p>To reduce the weight of 20 vol% Al2O3-particle-dispersed Mg (Al2O3/Mg) compacts produced by spark plasma sintering (SPS), which are much harder than practical high strength AZ91 Mg alloys, 20/0/20 vol% laminated SPS compacts sandwiching a lightweight 0 vol% Al2O3/Mg (0 vol%) layer between two 20 vol% Al2O3/Mg (20 vol%) layers were fabricated by a mechanical milling/SPS process, and their microstructures and mechanical properties were investigated. The density of the 20/0/20 vol% laminated SPS compacts was 1.88 Mg·m−3, and they could be lightened to approximately 80% of the weight of equivalent 20 vol% SPS compacts. The 20/0/20 vol% laminated SPS compacts had a slightly higher hardness than the 20 vol% SPS compacts and a much higher hardness than AZ91 alloys. The bending strength of the 20/0/20 vol% laminated SPS compacts was almost the same as that of the 20 vol% SPS compacts, and was higher than the value calculated from those of the 20 and 0 vol% SPS compacts using the rule of mixtures. A new phase appeared at the flat interface between the 20 and 0 vol% layers with excellent adhesion to the adjoining layers, so this phase probably had a strong effect on the bending strength of the 20/0/20 vol% laminated SPS compacts. The new phase generated a monotonically decreasing hardness gradient from the 20 vol% layer to the 0 vol% layer and was formed by diffusion of Al and O from the 20 vol% layer and diffusion of Mg from the 0 vol% layer. The new phase most likely consisted of αMg, MgO, and Mg17Al12, and the concentrations of Al in the αMg, MgO, and Mg17Al12 components of this phase were considered to decrease from the 20 vol% layer to the 0 vol% layer.</p>
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 58 (2), 206-210, 2017
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679229965440
-
- NII論文ID
- 130005297182
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 027871897
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可