Pseudocapacitive Behavior of Ag₃PO₄ Nanospheres Prepared by a Sonochemical Process
-
- Zheng Chengxiang
- School of Science, Lanzhou University of Technology
-
- Yang Hua
- School of Science, Lanzhou University of Technology
-
- Yang Yang
- School of Science, Lanzhou University of Technology
書誌事項
- タイトル別名
-
- Pseudocapacitive Behavior of Ag<sub>3</sub>PO<sub>4</sub> Nanospheres Prepared by a Sonochemical Process
この論文をさがす
抄録
<p>Ag3PO4 nanospheres with an average size of ~300 nm were synthesized via a sonochemical process. The electrochemical performances of the as-synthesized Ag3PO4 nanospheres in aqueous KOH electrolyte with different concentrations were investigated by cyclic voltammetry, galvanostatic charge-discharge and electrochemical impedance spectroscopy. The measured cyclic voltammetry curves as well as charge-discharge curves reveal a good pseudocapacitive behavior of Ag3PO4 nanospheres. In a 1 M KOH electrolyte at a current density of 0.5 mA cm−2, the specific capacitance of Ag3PO4 nanospheres is obtained to be 832 F g−1. However, Ag3PO4 nanospheres exhibit an inferior charge-discharge cycling stability, which could be due to the formation of Ag2O during the cycling process.</p>
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 58 (2), 298-301, 2017
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679229967488
-
- NII論文ID
- 130005297189
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 027872107
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可