Electrochemical Preparation of Porous Ti–13Zr–13Nb Alloy and It's Corrosion Behavior in Ringer's Solution
-
- Yu Tang
- School of Resource and Environmental Science, Wuhan University
-
- Yin Huayi
- School of Resource and Environmental Science, Wuhan University
-
- Zhou Yi
- School of Stomatology, Wuhan University
-
- Wang Yining
- School of Stomatology, Wuhan University
-
- Zhu Hua
- School of Resource and Environmental Science, Wuhan University
-
- Wang Dihua
- School of Resource and Environmental Science, Wuhan University
この論文をさがす
抄録
<p>A ternary titanium alloy (Ti-13Zr-13Nb (TZN)) was prepared by direct electrochemical reduction of a sintered TiO2-ZrO2-Nb2O5 mixture in molten CaCl2 at 850℃ with an energy consumption of 17 kWh/kg-alloy. The electrolytic Ti alloy was well sintered with bright metallic luster, and it was in α+β dual phase and of porous structure with designed composition. The corrosion behaviors of the obtained TZN in Ringer's solution were tested by open circuit potential and potentiodynamic polarization measurements. The results show that the corrosion rate of the porous electrolytic TZN alloy is lower than that of commercial pure titanium (CP-Ti) after being immersed in Ringer's solution for 10 days. The one-step electro-reduction of mixed oxide powers in molten salts could be an energy efficient and straightforward way to prepare porous implantable alloys.</p>
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 58 (3), 326-330, 2017
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679230787456
-
- NII論文ID
- 130005397751
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 028017179
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可