Stress Corrosion Cracking and Corrosion Resistance of Mg–6%Al–1%Zn–2%Ca Extruded Magnesium Alloys
-
- Yuasa Motohiro
- Structural Materials Research Institute, National Institute of Advanced Industrial Science and Technology
-
- Yukutake Eitaro
- Industrial Technology Institute of Ibaraki Prefecture
-
- Huang Xinsheng
- Structural Materials Research Institute, National Institute of Advanced Industrial Science and Technology
-
- Suzuki Kazutaka
- Structural Materials Research Institute, National Institute of Advanced Industrial Science and Technology
-
- Saito Naobumi
- Structural Materials Research Institute, National Institute of Advanced Industrial Science and Technology
-
- Chino Yasumasa
- Structural Materials Research Institute, National Institute of Advanced Industrial Science and Technology
この論文をさがす
抄録
<p>Stress corrosion cracking (SCC) and corrosion resistance of Mg–6 mass%Al–1 mass%Zn–2 mass%Ca (AZX612) extruded alloy were investigated by slow strain rate tensile tests (SSRT) in 0.01 M NaCl solution and immersion tests in 5 mass% NaCl solution, and compared with those of Mg–6 mass%Al–1 mass%Zn (AZ61) extruded alloy. In the SSRT in the salt solution, as-received AZX612 exhibited lower elongation and higher SCC susceptibility than those of as-received AZ61, indicating that calcium addition in Mg–Al alloy deteriorated SCC resistance. On the other hand, after solution treatment, improvement of elongation and SCC susceptibility occurred in both the alloys. Observation of surface profiles for AZX612 and AZ61 after the SSRT in salt solution revealed that corrosion pits on surface likely initiated SCC in both the alloys. The results of immersion tests showed the same tendency with those of SSRT in salt solution. It is suggested that SCC resistance of AZX612 and AZ61 was likely related to the microstructural change accompanied with calcium addition and solution treatment such as the change in distributions of Al2Ca phase and Al-rich phase.</p><p> </p><p>This Paper was Originally Published in Japanese in J. JILM 66 (2016) 266–272.</p>
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 58 (9), 1257-1263, 2017
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679230796288
-
- NII論文ID
- 130006003841
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 028470540
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可