- Influence of Thermal Effusivity of Ceramic Dense Mold on Microwave-heating of Carbon Fiber Reinforced Plastic
- タンソ センイ キョウカ ジュシ ノ マイクロハ カネツ ニ セラミックスチミツセイケイガタ ノ ネツ シントウリツ ガ オヨボス エイキョウ
この論文をさがす
抄録
<p>In order to develop a novel high-speed forming method of carbon fiber reinforced plastic (CFRP) using microwave-irradiation, the heating condition of CFRP was investigated using mullite dense compact with low thermal effusivity (3.8 kJ/m2·s1/2·K) and alumina dense compact with high thermal effusivity (10.3 kJ/m2·s1/2·K) as a mold. It was found that mullite dense compact with low thermal effusivity was useful as a mold material for the novel high-speed forming method of CFRP using microwave-irradiation because the mullite dense compact could heat CFRP 1.25 times faster than the alumina dense compact. Furthermore, it was found that the thermal conductivity of the densified mullite compact was affected by the size of the sintered grains, and the densified mullite compact was a mold material having heat resistance and mechanical strength for CFRP molding conditions.</p>
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 64 (10), 532-537, 2017
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206310261760
-
- NII論文ID
- 130007311762
- 40021362508
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 028613313
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可