Formation of non-equilibrium phases in the alloy systems with positive heat of mixing by mechanical alloying 正の混合熱を持つ合金系でのメカニカルアロイングによる非平衡相の形成
Access this Article
Search this Article
Author
Bibliographic Information
- Title
-
Formation of non-equilibrium phases in the alloy systems with positive heat of mixing by mechanical alloying
- Other Title
-
正の混合熱を持つ合金系でのメカニカルアロイングによる非平衡相の形成
- Author
-
上西, 啓介
- Author(Another name)
-
ウエニシ, ケイスケ
- University
-
京都大学
- Types of degree
-
工学博士
- Grant ID
-
乙第7951号
- Degree year
-
1992-09-24
Note and Description
博士論文
Table of Contents
- 論文目録 / (0001.jp2)
- CHAPTER 1 General introduction / p1 (0006.jp2)
- 1.1 Non-equilibrium phases / p1 (0006.jp2)
- 1.2 Mechanical alloying / p2 (0007.jp2)
- 1.3 Trends of the recent studies on MA and the purpose of this thesis / p3 (0007.jp2)
- References / p11 (0011.jp2)
- CHAPTER 2 Formation of super-saturated solid solution in the Ag-Cu system / p16 (0014.jp2)
- 2.1 Introduction / p16 (0014.jp2)
- 2.2 Experimental / p18 (0015.jp2)
- 2.3 Results and discussion / p22 (0017.jp2)
- 2.4 Conclusion / p42 (0027.jp2)
- References / p43 (0027.jp2)
- CHAPTER 3 Mechanical alloying in the Fe-Cu system / p44 (0028.jp2)
- 3.1 Introduction / p44 (0028.jp2)
- 3.2 Experimental / p44 (0028.jp2)
- 3.3 Results and discussion / p47 (0029.jp2)
- 3.4 Conclusion / p66 (0039.jp2)
- References / p67 (0039.jp2)
- CHAPTER 4 Non-equilibrium phases formation in the Fe-Ag-Cu system / p68 (0040.jp2)
- 4.1 Introduction / p68 (0040.jp2)
- 4.2 Experimental / p69 (0040.jp2)
- 4.3 Results and discussion / p69 (0040.jp2)
- 4.4 Conclusion / p83 (0047.jp2)
- References / p85 (0048.jp2)
- CHAPTER 5 Formation of non-equilibrium phases by repeated rolling / p86 (0049.jp2)
- 5.1 Introduction / p86 (0049.jp2)
- 5.2 Experimental / p86 (0049.jp2)
- 5.3 Results and discussion / p88 (0050.jp2)
- 5.4 Conclusion / p96 (0054.jp2)
- References / p98 (0055.jp2)
- CHAPTER 6 Thermodynamical analysis / p99 (0055.jp2)
- 6.1 Introduction / p99 (0055.jp2)
- 6.2 Results and discussion / p99 (0055.jp2)
- 6.3 Conclusion / p109 (0060.jp2)
- References / p110 (0061.jp2)
- CHAPTER 7 Summary / p111 (0061.jp2)