Controlling heat transfer in mold by flux film in continuous casting of steel 鋼の連続鋳造時のフラックスフィルムによる鋳型内伝熱制御
この論文にアクセスする
この論文をさがす
著者
書誌事項
- タイトル
-
Controlling heat transfer in mold by flux film in continuous casting of steel
- タイトル別名
-
鋼の連続鋳造時のフラックスフィルムによる鋳型内伝熱制御
- 著者名
-
趙, 重郁
- 著者別名
-
チョウ, ジュンウク
- 学位授与大学
-
東北大学
- 取得学位
-
博士(工学)
- 学位授与番号
-
甲第6608号
- 学位授与年月日
-
1998-09-09
注記・抄録
博士論文
目次
- CONTENTS / p1 (0003.jp2)
- Chapter 1 Introduction / p1 (0006.jp2)
- 1.1 Background / p1 (0006.jp2)
- 1.2 Previous studies / p5 (0010.jp2)
- 1.3 Purpose of this study / p20 (0025.jp2)
- 1.4 Outline of this study / p22 (0027.jp2)
- References / p23 (0028.jp2)
- Chapter 2 Radiative Heat Transfer through Mold Flux Film during Initial Solidification in Continuous Casting of Steel / p27 (0032.jp2)
- 2.1 Introduction / p27 (0032.jp2)
- 2.2 Experimental / p28 (0033.jp2)
- 2.3 Results and discussion / p32 (0037.jp2)
- 2.4 Summary / p57 (0062.jp2)
- References / p62 (0067.jp2)
- Chapter 3 Thermal Resistance at the Interface between Mold Flux Film and Mold for Continuous Casting of Steels / p64 (0069.jp2)
- 3.1 Introduction / p64 (0069.jp2)
- 3.2 Experimental / p66 (0071.jp2)
- 3.3 Numerical calculation / p71 (0076.jp2)
- 3.4 Results / p74 (0079.jp2)
- 3.5 Discussion / p82 (0087.jp2)
- 3.6 Summary / p91 (0096.jp2)
- References / p93 (0098.jp2)
- Chapter 4 Heat Transfer across Mold Flux Film in Mold during Initial Solidification in Continuous Casting of Steel / p95 (0100.jp2)
- 4.1 Introduction / p95 (0100.jp2)
- 4.2 Method of calculation and preliminary results / p96 (0101.jp2)
- 4.3 Results and discussion / p110 (0115.jp2)
- 4.4 Summary / p126 (0131.jp2)
- Appendix A / p128 (0133.jp2)
- Appendix B / p129 (0134.jp2)
- References / p132 (0137.jp2)
- Chapter 5 In-situ Observation of Crystallization of Mold Flux for High Speed Continuous Casting of Steel Slabs / p135 (0140.jp2)
- 5.1 Introduction / p135 (0140.jp2)
- 5.2 Experimental / p136 (0141.jp2)
- 5.3 Results and discussion / p137 (0142.jp2)
- 5.4 Summary / p151 (0156.jp2)
- References / p154 (0159.jp2)
- Chapter 6 Conclusions / p156 (0161.jp2)