<jats:p>Fatigue failure is normally initiated at the surface of a material. For some materials, failure can be initiated both at the surface and the interior. This twofold materials behaviour in fatigue is represented by a stepwise shape in the <jats:italic>S</jats:italic>–<jats:italic>N</jats:italic> curve. An internal failure mode is especially important for fatigue life in the gigacycle range, as this mode is predominant at low stress ranges.</jats:p><jats:p>Materials with a hardened surface fail from the surface only at high stresses, and at low stresses from the inside, forming a fish‐eye facet on the fracture surface. Exactly the same behaviour can be observed for materials without a hard surface, even at elevated temperatures. This paper displays some of the results obtained at NRIM and discusses possible interpretations.</jats:p>
収録刊行物
-
- Fatigue & Fracture of Engineering Materials & Structures
-
Fatigue & Fracture of Engineering Materials & Structures 22 (7), 601-607, 1999-07
Wiley
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1361699995555430784
-
- NII論文ID
- 80011204700
-
- ISSN
- 14602695
- 8756758X
-
- データソース種別
-
- Crossref
- CiNii Articles